High quality calendered polymeric PVC film with added pigment technology. The composition of the film gives a high dimensional stability characteristics and resistance to environmental effects over a long period of use.
The properties of this film allow it to be used widely for the application in car wrapping, in the production of high-quality emblems, decals, graphic sets, for long term design works for outdoor and indoor use.

Adhesive: acrylic-based, pressure sensitive
Liner: 140 g/m2 paper
Film thickness: 75 micron
The thickness of the adhesive layer: 25 micron
Tensile strength: > 20 N/mm2
Elongation: > 50 %
Gloss 60°: > 70 %
Adhesion:
Separation at an angle of 90°: 20 min - 520 N/m
The gap under the angle of 180°: after 20 minutes - 650 N/m
The gap under the angle of 180°: in 24 hours - 850 N/m
Dimensional stability: < 0.5 mm

Resistance to weather conditions:
white/black – 7 years in vertical position
color – 5 years in a vertical position
Metallics – 5 years in a vertical position

Note: the Index of stability can be changed in the decrease direction in case of improper storage, application and use.

Application temperature: from + 8°C to + 50°C on clean and dry surface
Temperature of use: from - 40°C to + 105°C
Storage: 2 years in protected place from sunlight
Indoor use at 23°C and 50 % relative humidity.

Recommended to use with cutter. White (gloss and matt) and transparent films are used for printing. It is not recommended to apply this type of films on defective, prone to corrosion and peeling surfaces. The surface for film deposition must be cleaned and degreased. The film belongs to the class of fire-resistant materials.